Polymaker Polyterra PLA - 4 Pack
Polymaker Polyterra PLA - 4 Pack
PolyTerra PLA is a bioplastic-based 3D printing filament that has been designed from the ground up to create the next generation of PLA, delivering ease of use, print quality, speed and reliability. It is a sustainable product with natural origins and for every spool produced, a tree is planted to give back to the earth.
- Perfect for multi-color printers
- Easy to print
- Good stiffness
Couldn't load pickup availability
Share


PolyTerra
PolyTerra PLA is a bioplastic filament for 3D printing where organic materials have been combined with PLA to reduce the plastic content and develop a more environmentally friendly filament.
PLA
PolyTerra prints just like PLA, so no print settings need to be changed, and the overhang and bridging capabilities can even outperform PLA. With a wide printing temperature range from 190 to 230°C, PolyTerra can be processed in all extrusion-based 3D printers.
Recommended settings
- Temperature in the nozzle: 190 - 230 ℃
- Build plate temperature: 25 - 60 ˚C
- Print speed: 30-70 mm/s
- Building surface materials: BuildTak®, glass, blue ribbon
- Cooling fan: ON
- For marble, we recommend using a 0.6 mm nozzle to avoid clogging
Technical Specifications
Basic Information |
|
Filament type |
PLA |
Diameter |
1.75mm |
Weight |
1.00 kg |
Length |
317 m |
Paint |
Brown |
|
|
Printing parameters |
|
Recommended minimum printing temperature |
190ºC |
Recommended maximum printing temperature |
230ºC |
Recommended min. bed temperature |
25ºC |
Recommended maximum bed temperature |
60ºC |
Recommendation My print speed |
30 mm/s |
Recommendation Max print speed |
70 mm/s |
Recommendation Max fan speed |
100% |
Recommended Indentation Min |
1mm |
Generally |
|
Specific gravity |
1.31 g/cm3 ISO 1183 |
Temperature |
|
Vicat softening temp. |
62.7 °C ISO 306 |
Extension |
|
Extension at break |
34.5% ISO 527 |
Bendability |
|
Bending strength |
39.6 MPa ISO 178 |
Flexural modulus |
2695 MPa ISO 178 |
Other |
|
Impact strength |
5.7 KJ/m2 ISO 179 |